Abstract:
Tin-doped indium oxide (ITO) has been widely used for various optoelectronic devices such as display panels, light-emitting diodes and solar cells due to its unique optical and electrical properties. Thin ITO films can be fabricated by a number of methods such as molecular beam epitaxy (MBE), laser ablation, dc sputtering, e-beam deposition, vapor phase deposition and electrochemical deposition and hydrothermal method. Apart from the conventional thin film form, one dimensional ITO nanorods or nanowires are attracting more research interest due to their high aspect ratio and large surface to volume ratio. For instance, a network made of ITO nanowires can exhibit high transparency (over 95 %) and high flexibility without losing its conducting property as reported recently. This network can be potentially used for bendable photovoltaic devices.
In this study, ITO nanorods or nanowires were fabricated using the vapor deposition, dc sputtering and e-beam deposition. The use of short ITO nanorods (100 nm) on glass and commercial ITO substrates as bottom electrodes to improve the charge collection of bulk heterojunction organic solar cells had been demonstrated. The growth mechanism of the ITO nanowires using different fabrication methods was discussed. The effects of the substrate temperature, oxygen content, choice of substrate and evaporation rate on the morphology, transmittance and sheet resistivity were investigated. When short ITO nanorods were incorporated into the bulk heterojunction organic solar cells, a significant improvement of the power conversion efficiency (PCE) was observed. The improvement was attributed to the improved charge collection.